Medium-Temperature Tawny Or Grey Strips Iron Oxide Desulfurizer
Reaction principle
When the desulfurization reaction temperature is high, reaching
200-400°C, the desulfurization mechanism of iron oxide is different
from that at room temperature, and it is generally considered to be
carried out in the following three steps:
i. Reduction
Fe304 with desulfurization activity at 200~400 °C, and the active
component in the desulfurizer is Fe20. Therefore, it should be fully reduced with reducing gas (H2 or C0) before use.
3Fe2O3+H2=2Fe304 +H2O. 3Fe2O3+CO=2Fe3O4+CO2
The reduction reaction is carried out at 170-300 °C, if the
reduction temperature exceeds 300 °C, excessive reduction will
occur, and iron oxide will be reduced to Fe304一FeO一Fe in turn, and when Fe0 or Fe appears, the activity of the
desulfurizer decreases significantly. Due to the exothermic and
counterheat of the reduction reaction head, a slight change in the
concentration of the reduction medium may cause overtemperature and
excessive reduction. Therefore, when carrying out the reduction
operation, the reduction temperature and the concentration of the
reduction medium should be strictly controlled.
ii. Organic sulfur conversion
The reduced Fe3O4 has a catalytic hydrogenation effect on some organic sulfur, and
the reaction is as follows:
COS+H2=H2S+C0. CS2+2H2=2H2S+CH4
iii. Hydrogen sulfide removal
In the presence of hydrogen, the desulfurization reaction of Fe3O4 is:
Fe3O4+3H2S+H2=3FeS+4H20
Remark: Expect the sizes shown above, we can customize it as per your
request.
Characteristics of Iron Oxide Desulfurizer:1.Take high quality Iron oxide as main components
2. High Desulfurization Accuracy: 20 Times higher than normal
Fe2O3.
3. Fast Speed Reaction: 5~6 Times faster than normal Fe2O3.
4. Working Penetrate Sulfur Capacity: 5~6 Times faster than normal
Fe2O3.
5. High strength and water resistance: After boiling 2 hours or
impreganated 30days, it doesn't pulverize and strength keeps the
same.
6. Can be used in the absence of O2 or high CO2 conditions. In the
absence of oxygen, H2S removal sulfur capacity is more than 15%.It is widely is suitable for the fine removal of H2S in natural gas, (semi-)water gas, air gas, coke oven gas, shift
gas, C02 regenerative gas, food C02, synthetic raw gas, biogas,
waste gas and other famous gases, with a wide range of
applications.